Graphite Release Spray is a high purity - dry concentrated graphite lubricant and release agent containing fine graphite particles in a thermoplastic binder. It adheres strongly to:
- Metal
- Plastics
- Glass and many other Surfaces which require a highly effective anti-friction coating
Graphite Release Spray has been primarily formulated for use in the glass blowing and forming industry where it is used as a mould pre-treatment - as a molten glass flow improver and as a release agent.
APPLICATION
- Glass moulding mould pre-treatment and release agent
- Glass moulding (gob) flow improver
- Glass industry general and guide lubricant
- Dry film industrial lubricant
- Static discharge coating
- Electrically conductive contact lubricant
DIRECTIONS
Shake can thoroughly before use. Ensure that surfaces are dry and free from oil and grease (degrease with an Ambersil solvent cleaner if necessary).Apply a light - even coating from a distance of 15-25 cm. Once cured the film can be lightly burnished in order to provide a high quality finish to glassware.After use - always clean the actuator orifice by spraying upside-down until only gas escapes. At temperatures above 100oC the binding agent will decompose - leaving a graphite film that can be used as a release coating (without propellant)
- Appearance : Black
- Flashpoint : 11oC
- Drying time at room temperature : Touch dry in approx - 20 min
- Fully cured in 4 hours
- Temperature resistance of lacquer : 90OC approx
- Temperature resistance of graphite film : 250OC -300OC
- Packaging : 400ml aerosol
The product may be stored at normal ambient temperatures and has a shelf life of not less than 4 years with correct storage. Aerosols should always be stored below 50OC - away from direct heat and naked flame.